PA + 15CF 1,75mm

The PA + 15CF filament from ROSA3D is a combination of nylon and carbon fibers. The combination of the advantages of these two raw materials results in a product with extraordinary strength properties.

Prints made of PA + 15CF filament have the ability to work continuously at temperatures over 160°C.

PA + 15CF printouts can be successfully used as a replacement for steel elements in order to reduce the weight of the device or structure.

The PA + 15CF filament is easy to print and, thanks to the filling with carbon fiber, has a low processing shrinkage.

Recommended especially for semi-professionals and advanced users.

When printing with PA + 15CF, hardened steel nozzles are recommended (brass and aluminum nozzles are subject to abrasion), suggested nozzle size> 0.3 mm.

Recommended printing temperature 250-290 °C.

Recommended bed temperature: 100-120°C

TECHNICAL PARAMETERS PA + 15CF

Diameter (mm): 1.75 mm

Diameter tolerances (mm): +/- 0.05 mm

Ovality tolerance (mm): +/- 0.02 mm

Weight (g): 500 g (vacuum packed with a desiccant)

Printing temperature (° C): 250-290 ° C

Bed temperature (° C): 100-120 ° C

PHYSICAL PARAMETERS PA + 15CF

Density: 1.05 g / cm3

Odor: odorless

Charpy impact strength:

No notch - 55 kJ / m2 (ISO 179-1eU)

Notched - 15 kJ / m2 (ISO 179-1eA)

Tensile elongation (speed 5 mm / min, to break): 7% (ISO 527)

Tensile strength (speed 5 mm / min, to break): 50 MPa (ISO 527)

Tensile modulus of elasticity (speed 1 mm / min): 3650 MPa (ISO 527)

Vicat softening point: 168 ° C (ISO 306)